Partnerzy

Streszczenie:
The paper presents research on Ag+ ions implanted TiO2 thin layers with Raman spectroscopy imaging. The oxide layers were formed on Ti–6Al–4 V ELI titanium alloy substrates through a multistage hybrid oxidation process, which combines fluidised bed (FB) diffusive treatment at 640 °C for 8 h with physical vapor deposition (PVD) pulse magnetron sputtering. Silver ions were implanted into the TiO2 layer after the fluidised bed process using a Metal Vapour Vacuum Arc implanter to form an interface for further PVD oxidation and generate an antibacterial interface that prevents inflammation during top layer spallation and cracking under working conditions. The ion implantation process was preceded by Monte Carlo simulations modelling of the depth profiles using SRIM-2013.00 software. The fluence of implanted ions was 1 × 1017 cm-2, and the acceleration voltage was 60 kV. The modelled range at peak damage of the real Ag+ + Ag2+ + Ag3+ + Ag4+ profile was about 40 nm. Raman spectroscopy imaging, XRD, SEM and TEM observations were carried out to evaluate the effects of ion implantation, analyse oxide phases and determine the mechanism of TiO2 layer formation during combined oxidation. The layers exhibited both amorphous and crystalline characteristics, and the top surface area was composed of TiO2 rutile and anatase, as well as oxygen vacancies (at 750 cm-1) and crystalline TiO2 (at 310 cm-1). Amorphous TiO2 dominates in the middle and near substrate layer. The layer before the substrate is composed of Ag+ ion area (ca. 100 nm) and dense TiO2 mixture of rutile (236 cm-1) and partially anatase (141 cm-1). Ultimately, it has been found that the functionalisation of oxide layers using a multistage hybrid oxidation and ion implantation process leads to a change in oxygen concentration in the various TiO2 layers forming a highly defected and active top surface layer. The homogeneous multiphase oxide layers on Ti alloys implanted with Ag+ ions for generating an antibacterial interface might improve the bioactive properties, which in perspective might be essential for biomedical applications.

Słowa kluczowe:
Titanium alloys, Tio2 thin layers, Ag+ ion implantation, Rutile/anatase, Raman spectroscopy imaging

Streszczenie:
This study focuses on improving the wear resistance of cutting tools and extending their service life under intense mechanical, thermal, and radiation loads in nuclear power plant environments. This research investigates the potential of electrospark alloying (ESA) using W–Zr–B system electrodes obtained from disks synthesised by spark plasma sintering (SPS). The novelty of this work lies in the use of SPS-synthesised W–Zr–B ceramics, which are promising for nuclear applications due to their high thermal stability, radiation resistance and neutron absorption, as ESA electrodes. This work also establishes the relationship between discharge energy, coating microstructure and performance. The alloying electrode material exhibited a heterogeneous microstructure containing WB2, ZrB2, and minor zirconium oxides, with high hardness (26.6 ± 1.8 GPa) and density (8.88 g/cm3, porosity < 10%). ESA coatings formed on HS6-5-2 steel showed a hardened layer up to 30 µm thick and microhardness up to 1492 HV, nearly twice that of the substrate (~850 HV). Elemental analysis revealed enrichment of the surface with W, Zr, and B, which gradually decreased toward the substrate, confirming diffusion bonding. XRD analysis revealed a multiphase structure comprising WB2, ZrB2, WB4, and BCC/FCC solid solutions, indicating the formation of complex boride phases during the ESA process. Tribological tests demonstrated significantly enhanced wear resistance of ESA coatings. The results confirm the efficiency of ESA as a simple, low-cost, and energy-efficient method for local strengthening and restoration of cutting tools.

Słowa kluczowe:
electrospark alloying, W–Zr–B electrodes, SPS, coatings, phase composition, microstructure, hardness, steel