A novel metal matrix composites (MMC) with Mg matrix reinforced with natural filler in the form of Didymosphenia geminata frustules (algae with distinctive siliceous shells) are presented in this work. Pulse plasma sintering (PPS) was used to manufacture Mg-based composites with 1, 5 and 10 vol.% ceramic filler. As a reference, pure Mg was sintered. The results show that the addition of 1 vol.% Didymosphenia geminata frustules to the Mg matrix increases its corrosion resistance by supporting passivation reactions, and do not affect the morphology of L929 fibroblasts. Addition of 5 vol.% the filler does not cause cytotoxic effects, but it supports microgalvanic reactions leading to the greater corrosion rate. Higher content than 5 vol.% the filler causes significant microgalvanic corrosion, as well as increases cytotoxicity due to the greater micro-galvanic effect of the composites containing 10 and 15 vol.% diatoms. The results of contact angle measurements show the hydrophilic character of the investigated materials, with slightly increase in numerical values with addition of amount of ceramic reinforcement. The addition of Didymosphenia geminata frustules causes changes in a thermo-elastic properties such as mean apparent value of coefficient of thermal expansion (CTE) and thermal conductivity (λ). The addition of siliceous reinforcement resulted in a linear decrease of CTE and reduction in thermal conductivity over the entire temperature range. With the increasing addition of Didymosphenia geminata frustules, an increase in strength with a decrease in compressive strain is observed. In all composites an increase in microhardness was attained.
The results clearly indicate that filler in the form of Didymosphenia geminata frustules may significantly change the most important properties of pure Mg, indicating its wide potential in the application of Mg-based composites with a special focus on biomedical use.

Słowa kluczowe:
Metal-matrix composites (MMCs),Pulse plasma sintering (PPS),Ceramic filler,Microstructure,Properties

Streszczenie:
One promising strategy to reconstruct bone defects relies on 3D printed porous structures. In spite of several studies having been carried out to fabricate controlled, interconnected porous constructs, the control over surface features at, or below, the microscopic scale remains elusive for 3D polymeric scaffolds. In this study, we developed and refined a methodology which can be applied to homogeneously and reproducibly modify the surface of polymeric 3D printed scaffolds. We have demonstrated that the combination of a polymer solvent and the utilization of ultrasound was essential for achieving appropriate surface modification without damaging the structural integrity of the construct. The modification created on the scaffold profoundly affected the macroscopic and microscopic properties of the scaffold with an increased roughness, greater surface area, and reduced hydrophobicity. Furthermore, to assess the performance of such materials in bone tissue engineering, human mesenchymal stem cells (hMSC) were cultured in vitro on the scaffolds for up to 7 days. Our results demonstrate a stronger commitment toward early osteogenic differentiation of hMSC. Finally, we demonstrated that the increased in the specific surface area of the scaffold did not necessarily correlate with improved adsorption of protein and that other factors, such as surface chemistry and hydrophilicity, may also play a major role.

Słowa kluczowe:
surface modification, solvent treatment, polycaprolactone, BMP-2 adsorption

Streszczenie:
One promising strategy to reconstruct osteochondral defects relies on 3D bioprinted three-zonal structures comprised of hyaline cartilage, calcified cartilage, and subchondral bone. So far, several studies have pursued the regeneration of either hyaline cartilage or bone in vitro while—despite its key role in the osteochondral region—only few of them have targeted the calcified layer. In this work, we present a 3D biomimetic hydrogel scaffold containing β-tricalcium phosphate (TCP) for engineering calcified cartilage through a co-axial needle system implemented in extrusion-based bioprinting process. After a thorough bioink optimization, we showed that 0.5% w/v TCP is the optimal concentration forming stable scaffolds with high shape fidelity and endowed with biological properties relevant for the development of calcified cartilage. In particular, we investigate the effect induced by ceramic nano-particles over the differentiation capacity of bioprinted bone marrow-derived human mesenchymal stem cells in hydrogel scaffolds cultured up to 21 d in chondrogenic media. To confirm the potential of the presented approach to generate a functional in vitro model of calcified cartilage tissue, we evaluated quantitatively gene expression of relevant chondrogenic (COL1, COL2, COL10A1, ACAN) and osteogenic (ALPL, BGLAP) gene markers by means of RT-qPCR and qualitatively by means of fluorescence immunocytochemistry.

Słowa kluczowe:
alginate, gelatin methacrylate, ß-tricalcium phosphate TCP, bioprinting, coaxial needle, calcified cartilage

Streszczenie:
Injection of cell‐laden scaffolds in the form of mesoscopic particles directly to the site of treatment is one of the most promising approaches to tissue regeneration. Here, a novel and highly efficient method is presented for preparation of porous microbeads of tailorable dimensions (in the range ≈300–1500 mm) and with a uniform and fully interconnected internal porous texture. The method starts with generation of a monodisperse oil‐in‐water emulsion inside a flow‐focusing microfluidic device. This emulsion is later broken‐up, with the use of electric field, into mesoscopic double droplets, that in turn serve as a template for the porous microbeads. By tuning the amplitude and frequency of the electric pulses, the template droplets and the resulting porous bead scaffolds are precisely produced. Furthermore, a model of pulsed electrodripping is proposed that predicts the size of the template droplets as a function of the applied voltage. To prove the potential of the porous microbeads as cell carries, they are tested with human mesenchymal stem cells and hepatic cells, with their viability and degree of microbead colonization being monitored. Finally, the presented porous microbeads are benchmarked against conventional microparticles with nonhomogenous internal texture, revealing their superior performance.

Streszczenie:
In this paper, the effect of the presence of L929 fibroblast cells and a cyclic load application on the kinetics of the degradation of amorphous PLGA films was examined. Complex micro and nano morphological, mechanical and physico-chemical studies were performed to assess the degradation of the tested material. For this purpose, molecular weight, glass transition temperature, specimen morphology (SEM, μCT) and topography (AFM) as well as the stiffness of the material were measured. The study showed that the presence of living cells along with a mechanical load accelerates the PLGA degradation in comparison to the degradation occurring in acellular media: PBS and DMEM. The drop in molecular weight observed was accompanied by a distinct increase in the tensile modulus and surface roughness, especially in the case of the film degradation in the presence of cells. The suspected cause of the rise in stiffness during the degradation of PLGA films is a reduction in the molecular mobility of the distinctive superficial layer resulting from severe structural changes caused by the surface degradation. In conclusion, all the micro and nanoscale properties of amorphous PLGA considered in the study are sensitive to the presence of L929 cells, as well as to a cyclic load applied during the degradation process.

Słowa kluczowe:
L929, aliphatic polyester, stiffness rise

Streszczenie:
In vitro degradation behavior of squeeze cast (CAST) and equal channel angular pressed (ECAP) ZM21 magnesium alloy (2.0 wt% Zn-0.98 wt% Mn) was studied using immersion tests up to 4 w in three different biological environments. Hanks' Balanced Salt Solution (Hanks), Earle's Balanced Salt Solution (Earle) and Eagle minimum essential medium supplemented with 10% (v/v) fetal bovine serum (E-MEM + 10% FBS) were used to investigate the effect of carbonate buffer system, organic compounds and material processing on the degradation behavior of the ZM21 alloy samples. Corrosion rate of the samples was evaluated by their Mg2 + ion release, weight loss and volume loss. In the first 24 h, the corrosion rate sequence of the CAST samples was as following: Hanks > E-MEM + 10% FBS > Earle. However, in longer immersion periods, the corrosion rate sequence was Earle > E-MEM + 10% FBS ≥ Hanks. Strong buffering effect provided by carbonate buffer system helped to maintain the pH avoiding drastic increase of the corrosion rate of ZM21 in the initial stage of immersion. Organic compounds also contributed to maintain the pH of the fluid. Moreover, they adsorbed on the sample surface and formed an additional barrier on the insoluble salt layer, which was effective to retard the corrosion of CAST samples. In case of ECAP, however, this effect was overcome by the occurrence of strong localized corrosion due to the lower pH of the medium. Corrosion of ECAP samples was much greater than that of CAST, especially in Hanks, due to higher sensitivity of ECAP to localized corrosion and the presence of Cl−.

The present work demonstrates the importance of using an appropriate solution for a reliable estimation of the degradation rate of Mg-base degradable implants in biological environments, and concludes that the most appropriate solution for this purpose is E-MEM + 10% FBS, which has the closest chemical composition to human blood plasma.

Słowa kluczowe:
ZM21 magnesium alloy, ECAP, Simulated body fluids, In vitro degradationBicomponent nanofibers, Biodegradation, Biopolymer

Streszczenie:
In the hereby presented work the authors describe a technique of high-compression-resistant biodegradable bone scaffold preparation. The methodology is based on the agglomeration of chitosan (CH) and chitosan/β-tricalcium phosphate (CH/TCP) microspheres and represents a novel approach to 3D matrices design for bone tissue engineering application. The materials were prepared from high deacetylation degree chitosan. The authors describe the method for scaffold fabrication, essential properties of the materials manufactured and the influence of various TCP concentrations on material morphology, mechanical properties (for dry and hydrated materials) and preliminary study on the interaction between CH or CH/TCP scaffolds and within cultured MG-63 osteoblast-like cells. The properties of the obtained materials were significantly affected by the calcium phosphate content, which had a particular influence on the granule microstructure, size distribution and inner biomaterial pore size. The water uptake ability was found to be lower for the materials enriched with the inorganic phase and tended to decrease with the increasing calcium phosphate concentration. The evaluation of mechanical properties has revealed that scaffolds produced with the usage of granule-based technology display a potential to be used as a load-bearing material since the Young’s modulus values were limited to the range of 200–500 MPa for dry materials and 15–20 MPa for the hydrated state of the scaffolds. The cell number, identified in three time points (48 h, 7 and 14 days) by Pico Green assay, was lower for the materials enriched with inorganic phase (75 % of control), however cell distribution, when compared to CH only biomaterial, was acknowledged as steadier on the surface of the material containing the highest calcium phosphate concentration.